ive been using 317L ss for a fair bit now mostly for tc but it defo needs less power to run it
as long as you don't glow it like a lightbulb its ok to use

its gota be worth ordering some 0.3 and 0.4 ss wire for yer squeeze
you can make it go pretty colours if you pulse it right
it seems a lot softer than kanthal so can be easier to work with but harder to rewick

[geordie_vaper]

Jan 1, 2017 21:19:10 GMT thebishman said:

Cheer mate. Just had a read. So does kanthal give off "oxides" too??

no idea, can send you some ss if you fancy seeing what its like?

[aaront903]

Ive just got a squeeze this evening by svb mods (pics at later dates)can someone explain the battery side of things?does it have low voltage protection?its my first mech for a very long time lol

[drunkenbum]

May 31, 2017 23:58:09 GMT aaront903 said:

Ive just got a squeeze this evening by svb mods (pics at later dates)can someone explain the battery side of things?does it have low voltage protection?its my first mech for a very long time lol

It does mate. It cuts off when the Bart gets to low. If the light comes on solid after firing its got loads left. Slow flash is like half empty and fast flash is nearly empty. It will just flash when it's empty and shut off

[aaront903]

Thanks pal

[striker42]

Squonk experience definitely a lot better now. Thanks phtumshk and drunkenbum for the advice.

[thebishman]

Jun 8, 2017 15:03:15 GMT striker42 said:

Squonk experience definitely a lot better now. Thanks phtumshk and drunkenbum for the advice.

Never tried anything but kanthal. How you finding it better striker?

[jtc]

Jun 8, 2017 16:07:47 GMT thebishman said:

Jun 8, 2017 15:03:15 GMT striker42 said:

Squonk experience definitely a lot better now. Thanks phtumshk and drunkenbum for the advice.

Never tried anything but kanthal. How you finding it better striker?

Never tried that myself.
Quicker ramp up time?

[striker42]

jtc has nailed it, quicker ramp up time.

[jtc]

Jun 8, 2017 16:18:24 GMT striker42 said:

jtc has nailed it, quicker ramp up time.

But ain't it nickel?
How can it be used in wattage mode?

[jtc]

The fact that it is a Nickel Chrome alloy allows it to be used in power mode. The Chrome changes the composition enough so that the nickel doesnt oxidize in a negative way.
Found that

[jtc]

Does it make the wicks black as bad as NI200 striker42?
Just I had terrible problems with that black gunk and it put me off

[phtumshk]

Jun 8, 2017 16:24:17 GMT jtc said:

Does it make the wicks black as bad as NI200 striker42 ?
Just I had terrible problems with that black gunk and it put me off

Not that bad IMO, Ive been using this constantly for a week full VG.


And this for about a month on/off.

[jtc]

Jun 8, 2017 16:48:47 GMT phtumshk said:

Jun 8, 2017 16:24:17 GMT jtc said:

Does it make the wicks black as bad as NI200 striker42 ?
Just I had terrible problems with that black gunk and it put me off

Not that bad IMO, Ive been using this constantly for a week full VG.


And this for about a month on/off.

Interesting
Can you dry burn it?

[phtumshk]

Jun 8, 2017 18:09:39 GMT jtc said:

Jun 8, 2017 16:48:47 GMT phtumshk said:

Not that bad IMO, Ive been using this constantly for a week full VG.


And this for about a month on/off.

Interesting
Can you dry burn it?

Dunno if its the dun thing but I have, quick burn under the tap good as new.